ASTM A335 P92 Alloy Seamless Steel Pipe

ASTM A335 P92 Alloy Seamless Steel Pipe
Alloy Seamless Steel Pipe, Alloy steel pipe, ASTM A335, ASTM A335 P92, p92, seamless steel pipe 
ASTM A335 P92 is the part of ASTM A335, The pipe shall be suitable for bending, flanging, and similar forming operations, and for fusion welding. The steel material shall conform to chemical composition, tensile property, and hardness requirements.
Each length of pipe shall be subjected to the hydrostatic test. Also, each pipe shall be examined by a non-destructive examination method in accordance to the required practices. The range of ASTM A335 P92 seamless alloy steel pipe sizes that may be examined by each method shall be subjected to the limitations in the scope of the respective practice.
The different mechanical test requirements for pipes, namely, transverse or longitudinal tension test, flattening test, and hardness or bend test are presented.Both ends of each crate will indicate the order no., heat no., dimensions, weight and bundles or as requested.
Chemical Requirements of ASTM A335 P92
UNS DesignationK92460
Carbon0.07–0.13
Manganese0.30–0.60
Phosphorus(max)0.02
Sulfur(max)0.01
Silicon0.50 max
Chromium8.50–9.50
Molybdenum0.30–0.60
V0.15-0.25
N0.03-0.07
Ni (max)0.4
Al(max)0.02
Cb0.04-0.09
W1.5-2.00
B0.001-0.006
Ti (max)0.01
Zr(max)0.01
 Mechanical Properties  of ASTM A335 P92
Tensile strength, min, (MPa)620
Yield strength, min, (MPa)440
Elongation, min, (%), L/T20/…
Material & Manufacture
Pipe may be either hot finished or cold drawn with the finishing heat treatment noted below.
Heat Treatment
  • A / N+T
  • N+T / Q+T
  • N+T
Mechanical Tests Specified of ASTM A335 P92
  • Transverse or Longitudinal Tension Test and Flattening Test, Hardness Test, or Bend Test
  • For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot. For small lots, at least one pipe shall be tested.
  • For material heat treated by the continuous process, tests shall be made on a sufficient number of pipe to constitute 5% of the lot, but in no case less than 2 pipe.
 Permitted tolerance for OD
ODPlus tolerance(+)Minus tolerance (-)
10.29—48.30.40.4
<48.3—-≤114.30.790.79
<114.3—≤219.11.590.79
<219.1—≤323.92.380.79
<323.9±1%
Wall thickness is average wall or according to ASME SA530.
Notes for Bend Test:
  • For pipe whose diameter exceeds NPS 25 and whose diameter to wall thickness ratio is 7.0 or less shall be subjected to the bend test instead of the flattening test.
  • Other pipe whose diameter equals or exceeds NPS 10 may be given the bend test in place of the flattening test subject to the approval of the purchaser.
  • The bend test specimens shall be bent at room temperature through 180 without cracking on the outside of the bent portion.
标签：

此博客中的热门博文

ASTM A213 T11 Seamless tube

ASTM A213 ,  ASTM A213 T11 ,  boiler tube ,  Heat exchanger tube ,  heat exchanger tubes ,  steel tubes ,  Tubing ASTM A213 T11 is the part of ASTM A213 Standard Specification for Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, Heat-Exchanger Tubes. These different requirements provide higher creep-rupture strength than normally achievable in similar grades without these different requirements. ASTM A213 T11 tubes shall be made by the seamless process and shall be either hot finished or cold finished, as specified. Grade TP347HFG shall be cold finished. Heat treatment shall be done separately and in addition to heating for hot forming. The ferritic alloy and ferritic stainless steels shall be reheated. On the other hand, austenitic stainless steel tubes shall be furnished in the heat-treated condition. Alternatively, immediately after hot forming, while the temperature of the tubes is not less than the minimum solution temperature, tubes may be individually quenched i
阅读全文

Pipe for cryogenic device

  Cryogenic piping refers to systems that are used in a wide range of industrial applications that require extremely low temperatures, generally around -300°F (150°C) or lower. Due to such low temperatures, cryogenic pipes face unique corrosion and deterioration challenges. Cyrogenic piping is also referred to as cold piping. Implement specifications such as ASME SA-333M, GB/T18984. The seamless steel tubes are applied for low temperature pressure vessel pipeline and low temperature heat exchanger pipeline. Usage Specification Steel Grade Seamless and Welding Nominal Pipe used for Low Temperature ASME SA -333M Gr.3, Gr.6, Gr.8 and so on Seamless Steel Pipe used for Low Temperature Pipeline GB/T18984 16MnDG, 06Ni3MoDG, 06Ni9MoDG and so on ASTM A333 (ASME S/A-333) Pipe grades permit low temperature service.  Mechanical requiremnts of ASTM A333 alloy pipe Grade Tensile Strength (MPa） Yield Point (MPa) Elongation (%) Y X Grade 3 ≥450 ≥240 ≥30 ≥20 Grade 6 ≥415 ≥240 ≥30 ≥16.5 Grade 8 ≥690 ≥5
阅读全文

Ceramic Lining Pipe and Elbow

Ceramic Lining Pipe and Elbow have very uniform coating of specially formulated ceramic material that is affixed to the inner of the pipe and gives a very smooth surface. Ceramics with very low friction factor at low impingement angles decreases the abrasion of materials maximally. Its low density makes it easy to carry and install. Furthermore, its diamond-like hardness, fine grain structure and superior mechanical strength are the unique features that make it a wide range of demanding applications, such as coal preparation, power generation, iron and steelmaking, cement, asphalt, dredging, mining and mineral processing, oil and gas drilling. Metals have good ductility but poor resistance to abrasion - which means that abrasion prevention is required when metal pipes are used in high-temperature fluid catalyst service. On the other hand, ceramics possess great hardness and abrasion resistance, but they are brittle. Metal Ceramic double pipe is a hybrid pipe using metal as an outer pip
阅读全文