High strength cylinder pipe

High strength cylinder pipe has high strength & tenacity, brittle fracture resistance and good weldability. S700 and S890 high strength cylinder pipes also have good hardenability and uniform performance after heat treatment. They are especially suitable for manufacturing high strength cylinders with large OD, medium & large wall thickness.

Application Fields

High strength cylinder pipe are mainly used for hydraulic support of coal collection face, hydraulic cylinder, engineering machinery, ship lock and offshore platform etc.

Production Range

OD: 42mm-760mm
WT: 4mm-120mm

Standard and Steel Grade

GB/T 8162
GB/T 8163
GB/T 17396 or technical agreement.

Requirements for Mechanical Properties
Steel Grade	Delivery Condition	Tensile	Yield	Elongation	R.A.	Absorbed-engergy
		(MPa)	(MPa)	(%)	(%)	(J)
		Not Less Than
27SiMn	Quenching+Tempering	980	835	12	40	20℃(AKU2)	39
30CrMnSiA	Quenching+Tempering	1080	835	10	35	20℃(AKU2)	39
30CrMoA	Quenching+Tempering	930	735	12	50	20℃(AKU2)	71
20MnTiB	Quenching+Tempering	1050	930	10	45	20℃(AKU2)	50
S700	Quenching+Tempering	750	650	14	40	-20℃(AKV2)	47
S890	Quenching+Tempering	810	700	14	35	-40℃(AKV2)	60

Seamless pipe is used for supply or transportation of water, oil, gas and other liquids under the specification of seamless pipe (GB / T8163-1999).

Mechanical Properties(%) of GB/T8163 steel pipe

Standard codes	Models of steel tubes	Tensite strength（MPa）	Yield strength（MPa）	Elongation（％）
GB/T8163	10	335-475	≥205	≥24
	20	410-550	≥245	≥20
	Q345	490-665	≥325	≥21

Chemical Composition(%) of GB/T8163 steel pipe

Standard codes	Models of steel tubes	Chemical compositions（％）
Standard codes	Models of steel tubes	C	Si	Mn	P	S	Cr	Ni	Cu
GB/T8163	10	0.07-0.14	0.17-0.37	0.35-0.65	≤0.035	≤0.035	≤0.15	≤0.25	≤0.25
	20	0.17-0.24	0.17-0.37	0.35-0.65	≤0.035	≤0.035	≤0.25	≤0.25	≤0.25
	Q345	0.12-0.20	0.20-0.55	1.20-1.60	≤0.045	≤0.045	/	/	/

此博客中的热门博文

Silicon carbide alloy ceramic wear tube

Reaction bonded SiC is made by infiltrating compacts made of mixtures of SiC and carbon with liquid silicon. The silicon reacts with the carbon forming more SiC which bonds the initial SiC particles. Silicon carbide is formed in two ways, reaction bonding and sintering. Each forming method greatly affects the end microstructure. Reaction bonded SiC is made by infiltrating compacts made of mixtures of SiC and carbon with liquid silicon. The silicon reacts with the carbon forming more SiC which bonds the initial SiC particles. Sintered SiC is produced from pure SiC powder with non-oxide sintering aids. Conventional ceramic forming processes are used and the material is sintered in an inert atmosphere at temperatures up to 2000ºC or higher. Both forms of silicon carbide (SiC) are highly wear resistant with good mechanical properties, including high temperature strength and thermal shock resistance. Our engineers are always available to best advise you on the strengths and weaknesses of ea...

阅读全文

ASME SA333 Gr.6 Seamless Steel Pipe

ASME SA333 Gr.6 Seamless Steel Pipe alloy steel , ASME SA333 Gr.6 , astm a333 , ASTM A333 Gr.6 , ASTM A333 Grade 6 , gr 6 , seamless steel pipe ASTM A333 Standard covers seamless and welded steel pipe for low temperature service. The Grade 6 steel involved is similar to AISI 4032 low alloy steel. ASTM A333 Grade 6 pipe shall be made by the seamless or welding process with the addition of no filler metal in the welding operation. Seamless and Welded Steel Pipe size for Low-Temperature Service: Outer Dimensions: 19.05mm-114.3mm Wall Thickness:2.0mm-14 mm Length: max 16000mm Application: Seamless and Welded Steel Pipe for Low-Temperature Service. Steel grade: ASTM A333 Grade 6 Inspection and Test: Chemical Composition Inspection, Mechanical Properties Test Tensile Strength,Yield Strength, Elongation, Flaring, Flattening, Bending, Hardness, Impact Test Surface and Dimension Test,No-destructive Test, Hydrostatic Test. ASTM A333 Gr. 6 Chemical Compositions(...

阅读全文

Ultra high molecular weight polyethylene pipe

Ultra-high molecular weight polyethylene (UHMW-PE) is a new kind of engineering thermoplastics with more than 3 million viscosity-average molecular weight. What is UHMWPE Ultra-high molecular weight polyethylene pipe has superior performance over conventional HDPE pipe such as very high wear resistance, impact resistance, excellent resistance to internal pressure strength, resistance to environmental stress cracking, intrinsically self-lubricating, anti-adhesion, low temperature resistance and excellent chemical resistance. UHMWPE wear pipe UHMWPE pipe bend UHMWPE pipe for dredginge UHMWPE pipe with flangee Ultra-high molecular weight polyethylene (UHMW full name is ultra-high molecular weight polyethylene pipe) is a thermoplastic engineering plastics with an average molecular weight greater than 1.5 million, which is polymerized by ethylene and butadiene monomer under the action of a catalyst. Ultra high molecular weight polyethylene is superior in comprehensive performance, abrasion ...

阅读全文

Alloy pipe

搜索此博客